Synthesis and use of (polyfluoroaryl)fluoroanions of aluminum, gallium and indium

ABSTRACT

Salts of (polyfluoroaryl)fluoroanions of aluminum, gallium, and indium are described. The (polyfluoroaryl)fluoroanions have the formula [ER&#39;R&#34;R&#39;&#34;F].sup.⊖  wherein E is aluminum, gallium, or indium, wherein F is fluorine, and wherein R&#39;, R&#34;, and R&#39;&#34; is each a fluorinated phenyl, fluorinated biphenyl, or fluorinated polycyclic group.

This invention was made with Government support under Contract No. DE-FG02-86ER13511 awarded by the Department of Energy. The Government has certain rights in this invention.

REFERENCE TO RELATED APPLICATIONS

This application is a continuation-in-part of our prior application Ser. No. 09/222,326, filed Dec. 29, 1998, which is a continuation of application Ser. No. 08/912,617, filed Aug. 18, 1997, now U.S. Pat. No. 5,854,166, issued Dec. 29, 1998, which in turn claims priority of U.S. provisional application Ser. No. 60/024,190, filed Aug. 19, 1996.

BACKGROUND OF THE INVENTION

This invention relates to the compositions of matter useful as a catalyst system, to a method for preparing these catalyst systems and to a method for polymerization utilizing the catalyst system.

The use of soluble Ziegler-Natta type catalysts in the polymerization of olefins is well known in the prior art. In general, such systems include a Group IV-B metal compound and a metal or metalloid alkyl cocatalyst, such as aluminum alkyl cocatalyst. More broadly, it may be said to include a mixture of a Group I-III metal alkyl and a transition metal complex from Group IVB-VB metals, particularly titanium, zirconium, or hafnium with aluminum alkyl cocatalysts.

First generation cocatalyst systems for homogeneous metallocene Ziegler-Natta olefin polymerization, alkylaluminum chlorides (AlR₂ Cl), exhibit low ethylene polymerization activity levels and no propylene polymerization activity. Second generation cocatalyst systems, utilizing methyl aluminoxane (MAO), raise activities by several orders of magnitude. In practice however, a large stoichiometric excess of MAO over catalyst ranging from several hundred to ten thousand must be employed to have good activities and stereoselectivities. Moreover, it has not been possible to isolate characterizable metallocene active species using MAO. The third generation of cocatalyst, B(C₆ F₅)₃, proves to be far more efficient while utilizing a 1:1 catalyst-cocatalyst ratio. Although active catalyst species generated with B(C₆ F₅)₃ are isolable and characterizable, the anion MeB(C₆ F₅)₃.sup.⊖ formed after Me.sup.⊖ abstraction from metallocene dimethyl complexes is weakly coordinated to the electron-deficient metal center, thus resulting in a decrease of certain catalytic activities. The recently developed B(C₆ F₅)₄.sup.⊖ type of non-coordinating anion exhibits some of the highest reported catalytic activities, but such catalysts have proven difficult to obtain in the pure state due to poor thermal stability and poor crystallizability, which is crucial for long-lived catalysts and for understanding the role of true catalytic species in the catalysis for the future catalyst design. Synthetically, it also takes two more steps to prepare such an anion than for the neutral organo-Lewis acid.

SUMMARY OF THE INVENTION

Accordingly, it is an object of the subject invention to prepare and utilize a new class of olefin polymerization catalytic system.

A further object of the subject invention is a catalytic system which permits better control over molecular weight, molecular distribution, stereoselectivity, and comonomer incorporation.

Another object of the subject invention is a Ziegler-Natta type catalytic system which reduces the use of excess cocatalyst and activates previously unresponsive metallocenes.

These and other objects are attained by the subject invention whereby in one embodiment, a salt of a strong organo-Lewis acid, such as a (perfluoroaryl)aluminate anion and in particular tris(2,2',2"-nonafluorobiphenyl)fluoroaluminate (PBA.sup.⊖) is utilized as a highly efficient cocatalyst for metallocene-mediated olefin polymerization. PBA.sup.⊖ exhibits higher catalytic activities and can activate previously unresponsive metallocenes. The synthesis of the stable perfluoroaryl aluminum anion, tris(2,2',2"-nonafluorobiphenyl)fluoroaluminate (PBA.sup.⊖) is accomplished with the use of sterically encumbered perfluorobiphenyl ligand.

In one embodiment of the subject invention a salt of a strong organo-Lewis acid, such as a fluoroaryl metal compound, is utilized to synthesize stoichiometrically precise, isolable/crystallographically characterizable, highly active "cation-like" metallocene polymerization catalysts.

In the subject application, "Cp" represents a cyclopentadienyl radical which may be substituted or unsubstituted, and: (Cp)(Cp') or Cp-A-Cp' and Cp and Cp' are the same or different cyclopentadienyl ring substituted with zero to five substituent groups β and each substituent group β is, independently, a radical which can be hydrocarbyl, substituted-hydrocarbyl, halocarbyl, substituted-halocarbyl, hydrocarbyl-substituted organometalloid, halocarbyl-substituted organometalloid, or halogen radicals (the size of the radicals need not be limited to maintain catalytic activity; however, generally the radical will be a C₁ to C₂₀ radical) or Cp and Cp' are a cyclopentadienyl ring in which any two adjacent R groups are joined forming a C₄ to C₂₀ ring to give a saturated or unsaturated polycyclic cyclopentadienyl ligand such as indenyl, tetrahydroindenyl, fluorenyl, or octahydrofluorenyl and A is a bridging group which restricts rotation of the two Cp-groups.

Each carbon atom in the cyclopentadienyl radical ("Cp") may be, independently, unsubstituted or substituted with the same or different radical group which is a hydrocarbyl, substituted-hydrocarbyl, halocarbyl, substituted-halocarbyl hydrocarbyl radicals in which adjacent substituents are joined to form a ring of 4 to 10 or more carbon atoms, hydrocarbyl- and halocarbyl-substituted organometalloid radicals and halogen radicals.

More specifically, a fluoroaryl metal compound such as ER'R"R'"F.sup.⊖ reacts with early transition metal or actinide alkyls to yield highly reactive cationic complexes:

    CpCp'MR.sub.2 +Ph.sub.3 C.sup.⊕ (ER'R"R'"F).sup.⊖ →[CpCp'MR].sup.⊕ [ER'R"R'"F].sup.⊖ +Ph.sub.3 CR(1)

where CpCp'=cyclopentadienyl, cyclopentadienyl substituted or bridged cyclopentadienyl ligands such as CpACp', indenyl Cp, allyl Cp, benzyl Cp; substituted indenyl Cp; substituted allyl Cp; substituted benzyl Cp; η⁵ -1,2-Me₂ C₅ H₃ ; η⁵ -1,3-(SiMe₃)₂ C₅ H₃ ; η⁵ -C₅ Me₅ ; (^(t) BuN)Me₂ Si(η⁵ -Me₄ C₅)

M=early transition metal or actinide, e.g., Ti, Zr, Hf, Th, U

R=PhCH₂, alkyl or aryl group (C≦20), hydride

R', R", R'"=fluorinated phenyls, fluorinated biphenyl or fluorinated polycyclic fused ring groups

E=Al, Ga, In

As a specific example of the above, the reaction of PBA.sup.⊖ with a variety of zirconocene dimethyl complexes proceeds rapidly and quantitatively to yield, after recrystallization from hydrocarbon solvents, in the catalytic complex set forth in Eq. 2.

    CpCp'MR.sub.2 +Ph.sub.3 C.sup.⊕ (ER'R"R'"F).sup.⊖ →CpCp'MR.sup.⊕ (ER'R"R'"F).sup.⊖ +Ph.sub.3 CR(2)

Such catalytic complexes have been found to be active homogeneous catalysts for α-olefin polymerization.

The cocatalyst of the subject invention may be referred to as ER_(F) 'R_(F) "R_(F) '"F.sup.⊕ ; where R', R", and R'" represent at least one and maybe more fluorinated biphenyls or other fluorinated polycyclic groups, such as naphthyl. Two of the biphenyls may be substituted with a phenyl or other aryl group. Both the biphenyls and the phenyl groups should be highly fluorinated, preferably with only one or two hydrogens on a group, and most preferably, as in PBA.sup.⊖ with no hydrogens and all fluorines. E represents Al, Ga or In.

BRIEF DESCRIPTION OF THE DRAWINGS

The cocatalyst system of the subject invention can be better understood with reference to the drawings wherein:

FIG. 1 is a reaction pathway for the synthesis of PBA.sup.⊖ ;

FIGS. 2a, 2b and 2c each show the reaction pathway for a catalyst system according to the subject invention.

DETAILED DESCRIPTION OF THE INVENTION

Under a variety of reaction conditions and ratios of reagents, the reaction of 2-nonafluorobiphenyl lithium and AlCl₃ all appear to lead to the formation of a compound with the formula Ar^(F) ₃ FAl.sup.⊖ Li.sup.⊕, resulting from fluoride abstraction by the strongly Lewis acidic trisperfluoro-biphenyl aluminum species generated in situ (FIG. 1). Ion exchange metathesis of this lithium salt with Ph₃ CCl results in the formation of stable trityl perfluorobiphenyl aluminate (PBA.sup.⊖). The structure of PBA.sup.⊖ has been characterized by X-ray diffraction and shows a non-associated trityl cation and aluminate anion.

Isolation and Characterization of Cationic Group 4 Complexes Derived from PBA

The reaction of PBA.sup.⊖ with various metallocene dialkyls readily generates the corresponding cationic complexes (FIGS. 2a-2c). The PBA.sup.⊖ anion is weakly coordinated to the metal center via F.sup.⊖ bridges in these complexes. This coordination is evident from the large downfield shift (≧30 ppm) of the Al--F F resonance in the ¹⁹ F NMR as compared to that of free PBA. This coordination lowers the symmetry of the cation portion as well. Furthermore, the coordinated anion is chiral. The relatively stable chirality of the anion stems from the bulkiness of the molecule which suppresses the rotation of the perfluoroaryl rings and renders the geometry fixed, resulting in nine (9) sets of characteristic resonances in the ¹⁹ F NMR. The influence of the anion chirality on the cation portion can be observed spectroscopically. In the reaction product of FIG. 2a, there are two diastereotopic CH₂ Ph protons with ² J value of 11.4 Hz and two magnetically nonequivalent Cp rings, which reflects the chiral environment of the coordinated anion.

With diastereotopic ring substitution in the metallocene, the structure of the reaction product shown in FIG. 2b offers unique NMR probes for a better understanding of the molecular structure. Coordination of an achiral anion such as CH₃ B(C₆ F₅)₃.sup.⊖ to the metal center of the cation portion of FIG. 2b results in the observation of two diastereotopic Cp methyls and three types of Cp ring protons having different chemical shifts. However, in the reaction product of FIG. 2b with a coordinated chiral anion, all the Cp methyls (four types) and Cp ring protons (six types) have different chemical shifts, clearly indicating the chiral induction of the anion.

Constrained geometry catalysts (FIG. 2c) activated by PBA exhibit two distinct silyl methyls and four different Cp methyls. The structure of the reaction product of FIG. 2c has been characterized by X-ray diffraction and reveals a chiral PBA.sup.⊖ anion coordinated via an F-bridge with a Zr--F bond length of (2.123)(6) Å. The Zr--CH₃ of bond distance of 2.21(1) Å is almost identical to that in (CGC)Zr(Me)[MeB(C₆ F₅)₃ ] (2.224(5)) Å, reflecting the cationic character of the zirconium center. In cases where the bulkiness of cationic portion is increased, thereby pushing the anion away from the coordinative periphery, the product formed from the reaction appears neither stable nor isolable, e.g., [(C₅ Me₅)₂ ZrMe.sup.⊕ PBA.sup.⊖ ]. However, this distant contact cation-anion pair exhibits extremely high activity for olefin polymerization when generated in situ.

Ph₃.sup.⊕ PBA.sup.⊖ has been synthesized in essentially quantitative yields as compared to the 30-50% yields experienced with B(C₆ F₅)₃, currently a very important Lewis acidic cocatalyst in the polyolefin industry. More particularly, reaction of Ph₃ C.sup.⊕ PBA.sup.⊖ with group 4 methyls proceeds cleanly to yield cationic complexes such as set forth below. ##STR1## CpCp'=Cp*=η⁵ -C₅ Me₅ =Cp"=η⁵ -1,2-Me₂ C₅ H₃

M=Ti, Zr, Hf

R=PhCH₂, CH₃, alkyl or aryl group with C≦20; hydride

CpCp'MR.sup.⊕ PBA.sup.⊖ may be any cyclopentadienyl, substituted cyclopentadienyl or bridged cyclopentadienyl complex paired with PBA.sup.⊖, such as Cp₂ ZrCH₂ Ph.sup.⊕ PBA.sup.⊖ ;

Cp₂ "ZrCH₃.sup.⊕ PBA.sup.⊖ ; (1,3-(SiMe₃)₂ C₅ H₃)₂ ZrCH₃.sup.⊕ PBA.sup.⊖ ; Cp'₂ ZrCH₃.sup.⊕ PBA.sup.⊖ ;

(CGC)ZrCH₃.sup.⊕ PBA.sup.⊖ ; (CGC)TiCH₃.sup.⊕ PBA.sup.⊖ ; and rac-Me₂ Si(Ind)₂ ZrCH₃.sup.⊕ PBA.sup.⊖ (CGC=^(t) BuN Me₂ Si(η⁵ -Me₄ C₅); (Ind=η⁵ -C₉ H₆).

For polymerization of olefin monomers, catalytic activities of the cations generated from PBA.sup.⊖ can be greater than those of monomeric cations generated from B(C₆ F₅)₃ in cases of bulky Cp and Cp' ligands presumably because PBA.sup.⊖ functions as a non-coordinating anion as compared to the weakly coordinating anion MeB(C₆ F₅)₃.sup.⊖. Polymerization reactions show very high activities for α-olefin polymerization, and identify PBA.sup.⊖ to be a truly non-coordinating anion. When polymerizing α-olefins larger than ethylene and particularly propylene and styrene, high isotacticity can be observed.

Experimental

Materials and Methods

All manipulations of air-sensitive materials were performed with rigorous exclusion of oxygen and moisture in flamed Schlenk-type glassware on a dual-manifold Schlenk line or interfaced to a high-vacuum line (10⁻⁶ Torr), or in a nitrogen-filled Vacuum Atmospheres glovebox with a high capacity recirculator (1-2 ppm O₂). Argon (Matheson, prepurified) and ethylene (Matheson, polymerization grade) were purified by passage through a supported MnO oxygen-removal column and an activated Davison 4 Å molecular sieve column. Ether solvents were purified by distillation from Na/K alloy/benzophenone ketyl. Hydrocarbon solvents (toluene, pentane) were distilled under nitrogen from Na/K alloy. All solvents for vacuum line manipulations were stored in vacuo over Na/K alloy in Teflon-valved bulbs. Deuterated solvents were obtained from Cambridge Isotope Laboratories (all ≧99 atom % D) and were freeze-pump-thaw degassed and dried over Na/K alloy and stored in resealable flasks. Non-halogenated solvents were dried over Na/K alloy and halogenated solvents were distilled over P₂ O₅ and stored over activated Davison 4 Å molecular sieves. BrC₆ F₅ (Aldrich) was vacuum distilled over P₂ O₅. AlCl₃, Ph₃ CCl and BuLi (1.6M in hexanes) were purchased from Aldrich. The zirconocene and titanocene complexes Cp₂ ZrMe₂ ; Cp₂ Zr(CH₂ Ph)₂ ; (1,2-Me₂ C₅ H₃)₂ ZrMe₂ ; [1,3-(SiMe₃)₂ C₅ H₃ ]₂ ZrMe₂ ; (C₅ Me₅)₂ ZrMe₂ ; Me₂ Si(Me₄ C₅)(^(t) BuN)ZrMe₂ ; and Me₂ Si(Me₄ C₅)^(t) BuNTiMe₂ were prepared according to known procedures.

Physical and Analytical Measurements

NMR spectra were recorded on either Varian VXR 300 (FT 300 MHz, ¹ H; 75 MHz, ¹³ C) or Varian Germini-300 (FT 300 MHz, ¹ H; 75 MHz, ¹³ C; 282 MHz, ¹⁹ F) instruments. Chemical shifts for ¹ H and ¹³ C spectra were referenced using internal solvent resonances and are reported relative to tetramethylsilane. ¹⁹ F NMR spectra were referenced to external CFCl₃. NMR experiments on air-sensitive samples were conducted in Teflon valve-sealed sample tubes (J. Young). Melting temperatures of polymers were measured by DSC (DSC 2920, TA Instruments, Inc.) from the second scan with a heating rate of 20° C./min.

EXAMPLE 1

Trityl Perfluorobiphenyl Aluminate, Ph₃ C.sup.⊕ DPBA.sup.⊖

n-Butyllithium (1.6M in hexanes, 25 mL, 40 mmol) was added dropwise to bromopentafluorobenzene (18.0 g, 9.1 mL, 72.9 mmol) in 100 mL of diethyl ether cooled by a cold-water bath. The mixture was then stirred for a further 12 h at room temperature. Removal of the solvent followed by vacuum sublimation at 60-65° C./10⁻⁴ Torr gave 12.0 g of 2-bromononafluorobiphenyl as a white crystalline solid. Yield: 83.3%. ¹⁹ F NMR (C₆ D₆, 23° C.): -126.77 (d,³ J^(F-F) =25.4 Hz, 1 F, F-3), -135.13 (d, ³ J_(F-F) =18.9 Hz, 1 F, F-6), -138.85 (d, ³ J_(F-F) =17.2 Hz, 2 F, F-2'/F-6'), -148.74 (t, ³ J_(F-F) =20.8 Hz, 1 F, F-4) -150.13 (t, ³ J_(F-F) =21.7 Hz, 1 F, F-4'), -154.33 (t, ³ J_(F-F) =21.4 Hz, 1 F, F-5), -160.75 (t, ³ J_(F-F) =23.9 Hz, 2 F, F-3'/F-5').

To the above 2-bromononafluorobipyhenyl (8.29 g, 21.0 mmol) in a mixed solvent of 70 mL of diethyl ether and 70 mL of pentane was gradually added 13.2 mL of n-butyllithium (1.6M in hexanes, 21.0 mmol) at -78° C. The mixture was stirred for an additional 2 h, and aluminum trichloride (0.67 g, 5.0 mmol) was then quickly added. The mixture was stirred at -78° C. for 1 h and the temperature was then allowed to slowly rise to room temperature. A white suspension resulted after stirring for an additional 12 h. The mixture was filtered and the solvent removed from the filtrate in vacuo. To the yellow sticky residue was added 100 mL of pentane and the mixture was stirred for 1 h. The resulting white solid was collected by filtration and dried in vacuo to give 3.88 g of Ar^(F) ₃ FAl.sup.⊖ Li.sup.⊕.OEt₂ : yield: 72.4% ¹ H NMR (C₇ D₈, 23° C.): 2.84 (q,J=7.2 Hz, 4H, 2-CH₂ O), 0.62 (t, J=7.2 Hz, 6H, 2CH₃ CH₂ O--). ¹⁹ F NMR (C₆ D₆, 23° C.): -122.80 (s, br, 3 F, F-3), -134.86 (s, 3 F, F-6), -139.12 (s, 6 F, F-2'/F-6'), -153.95 (t, ³ J_(F-F) =18.3 Hz, 3 F, F-4), -154.52 (t, ³ J_(F-F) =20.2 Hz, 6 F, F-4'/F-5 ), -162.95 (s, 6 F, F-3'/F-5'), -176.81 (s, br, 1 F, Al--F). The above lithium salt (1.74 g, 1.62 mmol) and Ph₃ CCl (0.48 g, 1.72 mmol) were suspended in pentane and stirred overnight and the resulting orange solid was collected by filtration and washed with pentane. The crude product was then redissolved in CH₂ Cl₂ and filtered through Celite to remove LiCl, followed by pentane addition to precipitate the orange solid. Recrystallization from CH₂ Cl₂ /pentane at -78° C. overnight gave 1.56 g of orange crystals of the title compound. Yield: 70.5%. Analytical and spectroscopic data for PBA are as follows: ¹ H NMR (CDCl₃, 23° C.): 8.25 (t, J=7.5 Hz, 3H, p-H, Ph), 7.86 (t, J=7.5 Hz, 6H, m-H, Ph), 7.64 (dd, J=8.4 Hz, J=1.2 Hz, 6H, o-H, Ph), 1.28 (m), 0.88(t) (pentane residue). ¹⁹ F NMR (CDCl₃, 23° C.): -121.05 (s, 3 F, F-3), -139.81 (s, 3 F, F-6), -141.19 (s, 6 F, F-2'/F-6), -156.93 (t, ³ J_(F-F) =18.3 Hz, 6 F, F-4/F-4'), -158.67 (s, 3 F, F-5). -165.32 (s, 6 F, F-3'/F-5'), -175.60 (s, br, 1 F, Al--F). Anal. Calcd for C₆₀ H₁₅ AlF₂₈. C₅ H₁₂ : C, 57.12; H, 1.99. Found: C, 57.16; H, 1.43.

EXAMPLE 2

Cp₂ ZrCH₂ Ph.sup.⊕(PBA).sup.⊖ (1)

Cp₂ Zr(CH₂ Ph)₂ (0.081 g, 0.20 mmol) and Ph₃ C.sup.⊕ PBA.sup.⊖ (0.261 g, 0.20 mmol) were charged in the glove box into a 25-mL reaction flask with a filter frit and the flask was reattached to the high vacuum line. Toluene (15 mL) was then vacuum-transferred into this flask at -78° C. The mixture was slowly allowed to warm to room temperature and stirred for 4 h. The volume of toluene was next reduced to 5 mL and 10 mL of pentane was condensed into the flask at -78° C. A suspension which formed was quickly filtered and the orange crystalline solid which was collected was dried under vacuum overnight. Yield, 0.22 g (84.4%). Large orange crystals were obtained by slowly cooling a pentane solution of the compound to -20° C. over a period of several days. ¹ H NMR (C₆ D₆, 23° C.): 6.95 (t, J=7.8 Hz, 2H, m-H, Ph), 6.80 (t, J=7.5 Hz, 1H, p-H, Ph), 6.46 (d, J=7.2 Hz, 2H, o-H, Ph), 5.45 (s, 5H, Cp), 5.42 (s, 5H, Cp), 2.47 (d, J=11.4 Hz, 1H, --CH₂), 1.92 (d, J=11.4 Hz, 1H, --CH₂). ¹⁹ F NMR (C₆ D₆, 23° C.): -117.09 (t, ³ J_(F-F) =20.5 Hz, 3 F), -133.17 (t, ³ J_(F-F) =15.2 Hz, 3 F), -138.60 (d, ³ J_(F-F) =27.3 Hz, 3 F), -139.53 (t, ³ J_(F-F) =21.2 Hz, 3 F), -146.34 (s, br, 1 F, Al--F), -152.01 (t, ³ J_(F-F) =24.3 Hz, 3 F), -153.15 (t, ³ J_(F-F) =20.9 Hz, 3 F), -153.92 (t, ³ J_(F-F) =18.3 Hz, 3 F), -160.82 (d, ³ J_(F-F) =21.4 Hz, 3 F), -162.52 (t, ³ J_(F-F) =24.53 Hz, 3 F), ¹³ C NMR (C₇ D₈, 23° C.): 129.20 (d, ³ J_(CH) =156.2 Hz, Ph), 128.26 (d, ³ J_(CH) =157.1 Hz, Ph), 127.52 (s, ipso-Ph), 125.42 (d, ³ J_(CH) =158.1 Hz, Ph), 114.77 (d, ³ J_(CH) =176.5 Hz, Cp), 66.68 (t, ³ J_(CH) =122.8 Hz, --CH₂), Anal. Calcd for C₅₃ H₁₇ AlF₂₈ Zr: C, 48.82; H, 1.31. Found: C, 48.77; H, 1.36.

EXAMPLE 3

Cp"₂ ZrMe.sup.⊕ PBA.sup.⊖ (2)

The procedure is the same as that of synthesis of Example 2 above. Yield: 81.7%. ¹ H NMR (C₂ D₂ Cl₄, 23° C.): δ 5.95 (s, br, 1H, C₅ H₃ Me₂), 5.77 (s, br, 1H, C₅ H₃ Me₂), 5.72 (s, br, 1H, (C₅ H₃ Me₂), 5.46 (s, br, 1H, C₅ H₃ Me₂), 5.70 (s, br, 1H, C₅ H₃ Me₂),5.40 (s, br, 1H, C₅ H₃ Me₂), 2.11 (s, 3H, C₅ H₃ Me₂), 1.98 (s, 3H, C₅ H₃ Me₂), 1.76 (s, 3H, C₅ H₃ Me₂), 1.70 (s, 3H, C₅ H₃ Me₂), 0.28 (d, ¹ J_(CH) =120.3 Hz, Zr--¹³ CH₃). ¹⁹ F NMR (C₂ D₂ Cl₄, 23° C.) is similar to the product of Example 2 except for a different chemical shift for the bridging F at -143.38 ppm. Anal. Calcd for C₅₁ H₂₁ AlF₂₈ Zr: C, 47.71; H, 1.65. Found: 47.46; H, 1.37.

EXAMPLE 4

C₅ H₃ (SiMe₃)₂ ZrMe.sup.⊕ PBA.sup.⊖ (3)

This complex was prepared as described in Example 2 above. It decomposes in toluene solution within 2 h at 25° C. and undergoes rapid decomposition to a myriad of unidentified products at higher temperatures. Characterization of the complex is based on very clean NMR scale reactions. This complex was generated in situ for polymerization studies. ¹ H NMR C₇ D₈, 23° C.): δ 6.88 (s, br, 1H, C₅ H₃ TMS₂), 6.71 (t, J=2.1 Hz, 1H, C₅ H₃ TMS₂), 6.31 (s, br, 1H, C₅ H₃ TMS₂), 6.23 (s, br, 1H, C₅ H₃ TMS₂), 5.79 (s, br, 1H, C₅ H₃ TMS₂), 5.71 (s, br, 1H, C₅ H₃ TMS₂), 0.70 (s, br, 3H, Zr--CH₃). 0.17 (s, 3H, C₅ H₃ TMS₂), 0.10 (s,3H, C₅ H₃ TMS₂), -0.05 (s, 3H, C₅ H₃ TMS₂), -0.07 (s, 3H, C₅ H₃ TMS₂). ¹⁹ F NMR (C₇ D₈, 23° C.): δ-112.12 (d, ³ J_(F-F) =12.2 Hz, 3 F), -133.22 (t, ³ J_(F-F) =15.5 Hz, 3 F), -137.49 (s, 3 F), -138.40 (t, ³ J_(F-F) =21.7 Hz, 3 F), -144.23 (s, br, 1 F, Al--F), -153.41 (m, 6 F), -154.15 (t, ³ J_(F-F) =21.2 Hz, 3 F), -161.80 (d, ³ J_(F-F) =18.3 Hz, 3 F), -162.82 (t, ³ J_(F-F) =21.4 Hz, 3 F).

EXAMPLE 5

(Cp'₂ ZrMe.sup.⊕ (PBA).sup.⊖ (4) is too thermally unstable at 25° C. to isolate. The ¹ H NMR monitored reaction of Cp'₂ ZrMe₂ and Ph₃ C.sup.⊕ PBA.sup.⊖ in C₂ D₂ Cl₄ clearly reveals the formation of Ph₃ CCH₃ (δ 2.15) and a broad singlet at δ 0.25 assignable to the ZrCH₃.sup.⊕ group. More than 4 Cp methyl resonances at δ 1.97-1.72 ppm with different intensities are observed indicating the decomposition. Complex 4 was generated in situ for polymerization studies. ¹⁹ F NMR (C₂ D₂ Cl₄): δ -114.77 (s, br, 3 F), -132.11 (t, ³ J_(F-F) =15.2 Hz, 3 F), -136.84 (t, ³ J_(F-F) =22.0 Hz, 3 F), -137.29 (s, br, 3 F), -150.90 (t, ³ J_(F-F) =20.9 Hz, 3 F), -151.85 (t, ³ J_(F-F) =23.9 Hz, 3 F), -152.47 (t, ³ J_(F-F) =24.5 Hz, 3 F), -155.78 (s, br, 1 F Al--F), -160.02 (d, ³ J_(F-F) =16.5 Hz, 3 F), -161.06 (t, ³ J_(F-F) =21.2 Hz, 3 F).

EXAMPLE 6

Me₂ Si(^(t) BuN)(C₅ Me₄)ZrMe.sup.⊕ PBA.sup.⊖

Me₂ Si(Me₄ C₅)(^(t) BuN)ZrMe₂ (0.148 g, 0.4 mmol) and Ph₃ C.sup.⊕ PBA.sup.⊖ (0.523, 0.4 mmol) were reacted in the same manner as in Example 2 to yield 0.35 g of the above complex as a white crystalline solid. Yield: 64.8%. The complex is quite soluble in pentane and cold pentane was used to wash the product. ¹ H NMR (C₇ D₈, 23° C.): 67 1.98 (s, 3H, C₅ Me₄), 1.82 (s, 3H, C₅ Me₄), 1.76 (s, 3H, C₅ Me₄), 1.27 (s, 3H, C₅ Me₄), 0.93 (s, 9H, N-^(t) Bu), 0.24 (s, 3H,SiMe₂), 0.18 (s, 3H,Zr--CH₃), 0.15 (s, 3H, SiMe₂), ¹⁹ F NMR (C₇ D₈,23° C.) δ -108.92 (s, br, 1 F, Al--F), -117.26 (s, br, 3 F), -133.19 (t, ³ J_(F-F) =12.1 Hz, 3 F), -139.25 (s, 6 F), -152.53 (t, J_(F-F) =21.2 Hz, 3 F), -153.00 (d, ³ J_(F-F) =21.2 Hz, 3 F), -153.00 (d, ³ J_(F-F) =21.4 Hz, 3 F), -153.76 (t, ³ J_(F-F) =24.3 Hz, 3 F), -160.94 (t, ³ J_(F-F) =22.6 Hz, 3 F), -162.80 (t, ³ J_(F-F) =21.4 Hz, 3 F). ¹³ C NMR (C₇ D₈, 23° C.): δ 130.19 (C₅ Me₄), 129.09 (C₅ Me₄), 127.18 (C₅ Me₄), 126.44 (C₅ Me₄), 124.33 (C₅ Me₄), 56.63 (N--CMe₃), 38.58 (q. J=120.6 Hz, N--CMe₃), 32.70 (q. J=120.8 Hz, Zr--CH₃), 15.75 (q, J=127.9 Hz, C₅ Me₄), 14.05 (q, J=128.0 Hz, C₅ Me₄), 12.00 (q, J=127.8 Hz, C₅ Me₄), 10.18 (q, J=128.1 Hz, C₅ Me₄), 8.49 (q, J=121.0 Hz, SiMe₂), 6.52 (q, J=120.9 Hz, SiMe₂). Anal. Calcd for C₅₂ H₃₀ AlF₂₈ NSiZr: C, 46.37;H, 2.25; N, 1.04. Found: C, 46.65; H, 2.13; N, 0.89.

EXAMPLE 7

Me₂ Si(Me₄ C₅)(^(t) BuN)TiMe.sup.⊕ PBA.sup.⊖

Me₂ Si(Me₄ C₅)(^(t) BuN)TiMe2 (0.065 g, 0.2 mmol) and Ph₃ C.sup.⊕ PBA.sup.⊖ (0.261, 0.2 mmol) were reacted in the same manner as in Example 2 to yield 0.12 g of the above complex as a yellow crystalline solid. Yield: 46.0%. Due to its good solubility in pentane, a significant amount of the product remained in the filtrate, resulting in a low isolated yield. An NMR scale reaction indicates the formation of the compound in quantitative yield when the isolation is not required. ¹ H NMR (C₆ D₆, 23° C.): δ 2.01 (s, 3H, C₅ Me₄), 1.72 (s, 3H, C₅ Me₄), 1.61 (s, 3H, C₅ Me₄), 1.20 (s, 3H, C₅ Me₄), 0.93 (s, 9H, N-^(t) Bu), 0.75 (d, J=3.9 Hz, 3H), 0.21 (s, H), 0.06 (s, 3H). ¹⁹ F NMR is similar to that of 3 except slightly for different chemical shifts. Anal. Calcd for C₅₂ H₃₀ AlF₂₈ NSiTi: C, 47.91; H, 2.32; N, 1.07. Found: C, 47.47; H, 1.96; N, 0.87.

EXAMPLE 8

Synthesis of Me₂ Si(Ind)₂ ZrMe.sup.⊕ PBA.sup.⊖

Me₂ Si(Ind)₂ ZrMe₂ (0.082 g, 0.20 mmol) and Ph₃ C.sup.⊕ PBA.sup.⊖ (0.261, 0.20 mmol) were reacted in the same manner as for the synthesis of 1 above to yield 0.19 g of the title complex as an orange crystalline solid. Yield: 68.6%. Two diastereomers are found in a 1.3:1 ratio. ¹ H NMR (C₆ D₆, 23° C.) for diastereomer A (56%): δ 7.45 (d, J=8.7 Hz, 1H, C₆ --HO, 7.27-6.88 (m, 4H, C₆ --H), 6.67 (t, J=7.5 Hz, 2H, C₆ --H), 5.88 (t, J=7.5 Hz, 1H, C₆ --H), 6.82 (t, J=3.3 Hz, 1H, C₅ -βH), 5.96 (d, J=3.3 Hz, 1H, C₅ -βH), 5.69 (s, br, 1H, C₅ -αH), 5.19 (d, J_(HF) =2.1 Hz, 3H,Zr--CH₃). Diastereomer B (44%): δ 7.94 (d, J=8.7 Hz, 1H, C₆ --H), 7.27-6.88 (m, 4H, C₆ --H), 6.58 (t, J=7.5 Hz, 2H, C₆ --H), 5.79 (t, J=7.5 Hz, 1H, C₆ --H), 6.42 (d, J=3.3 Hz, 1H, C₅ -βH), 5.85 (d, J=3.3 Hz, 1H, C₅ -βH), 5.56 (s, br, 1H, C₅ -αH), 4.80 (d, J=3.3 Hz, 1H, C₅ -αH), 0.46 (s, 3H, SiMe₂), 0.25 (s, 3H, SiMe₂), -0.64 (d, J_(HF) =2.1 Hz, 3H, Zr--CH₃). ¹⁹ F NMR (C₆ D₆, 23° C.) for diastereomer A (56%): δ -115.86 (s, br, 3 F), -132.23 (s, br, 1 F, Al--F), -133.76 (t, ³ J_(F-F) =18.3 Hz, 3 F), -138.53 (s, br, 3 F), -139.40 (t, ³ J_(F-F) 18.3 Hz, 3 F), -153.10 (t, ³ J_(F-F) =18.3 Hz, 3 F), -153.44 (t, ³ J_(F-F) =18.3 Hz, 3 F), -154.72 (t, ³ J_(F-F) =21.2 Hz, 3 F), -161.18 (t, ³ J_(F-F) =18.3 Hz, 3 F), -162.86 (t, ³ J_(F-F) =18.3 Hz, 3 F). Diastereomer B (44%): δ -113.48 (s, br, 3 F), -133.76 (t, ³ J_(F-F) =21.2 Hz, 3 F), -134.44 (s, br, 1 F, Al--F), -137.89 (s, br, 3 F), -139.09 (t, ³ J_(F-F) =18.3 Hz, 3 F), -153.10 (t, ³ J_(F-F) =18.3 Hz, 3 F), -153.28 (t, ³ J_(F-F) =18.3 Hz, 3 F), -153.73 (t, ³ J_(F-F) =18.3 Hz, 3 F), -161.03 (t, ³ J_(F-F) =18.3 Hz, 3 F), -162.68 (t, ³ J_(F-F) =18.3 Hz, 3 F). ¹³ C NMR (C₆ D₆, 23° C.): δ 134.02, 132.96, 132.43, 128.31, 127.67, 127.28, 126.95, 126.64, 126.21, 125.90, 125.81, 124.88, 124.20, 124.10, 123.57, 122.89, 122.01, 121.98 (C₆ -ring), 119.16, 116.56, 115.96, 114.94, 112.90, 112.79 (C₅ -ring), 91.82, 90.95, 89.30, 89.20, (C₅ -Si), 51.46, 51.73, (Zr--CH₃), -1.31, -2.13, -2.88, -3.51 (SiMe₂). Anal. Calcd for C₅₇ H₂₁ AlF₂₈ SiZr: C, 49.47; H, 1.53. Found: C, 49.09; H, 1.27.

EXAMPLES 9-16

Ethylene and Propylene Polymerization

In a glove box, a 250 mL flamed, 3-necked round-bottom flask equipped with a magnetic stirring bar was charged with metallocene (5-10 mg) and cocatalyst Ph₃ C.sup.⊕ PBA.sup.⊖, in a 1:1 molar ratio and the flask was then reattached to the high vacuum line. A measured amount of dry toluene (50 mL for this study) was next condensed onto the solids and the mixture was warmed to room temperature with stirring for 10 min to preactivate the catalyst. The resulting solution was then equilibrated at the desired reaction temperature using an external constant temperature bath. Gaseous ethylene or propylene was next introduced with rapid stirring and the pressure was maintained at 1.0 atm by means of a mercury bubbler. After a measured time interval, the reaction was quenched by the addition of 2% acidified methanol. The polymer was collected by filtration, washed with methanol, and dried on the high vacuum line overnight to a constant weight. Highly isotactic polypropylene is the result of propylene polymerization using PBA.sup.⊖ as a catalyst. The reaction parameters and results are set forth in the Table.

                                      TABLE                                        __________________________________________________________________________     Ethylene Polymerization Activities with Metallocene/Ph.sub.3 C.sup.⊕       PBA.sup.⊖ Catalysts and Polymer                                        Properties                                                                                                   activity.sup.a                                   Ex.          Tp μmol of                                                                         reaction                                                                            polymer                                                                             (g polymer/mol  T.sub.m.sup.d                                                                     AH.sub.u                      No.                                                                               Catalyst  (° C.)                                                                     cat.                                                                               time(min)                                                                           yields (g)                                                                          of cat · amt · h)                                                   M.sub.w.sup.c                                                                       Mw/Mn                                                                              (° C.)                                                                     (cal/g)                       __________________________________________________________________________      9 Cp.sub.2 ZrMe.sub.2                                                                      25 20  20   0    0                                                10 Cp"ZrMe.sub.2                                                                            25 20  30   0.18 1.80 × 10.sup.4                                                                 5.46 × 10.sup.5                                                               6.0 139.4                                                                             40.5                          11 (Cp.sup.TMS.sub.2).sub.2 ZrMe.sub.2                                                      25 15  2.0  0.54 1.08 × 10.sup.6                                                                 1.26 × 10.sup.6                                                               5.6 142.3                                                                             29                            12 Cp'.sub.2 ZrMe.sub.2                                                                     25 15  0.67 1.15 6.90 × 10.sup.6                                                                 8.97 × 10.sup.4                                                               4.6 138.0                                                                             53.9                          13 CGCZrMe.sub.2                                                                            25 15  10   0    0                                                14 CGCTiMe.sub.2                                                                            60 30  30   0.20 1.33 × 10.sup.4                                                                 2.05 × 10.sup.6                                                               3.9 139.2                                                                             19.5                          15 CGCTiMe.sub.2                                                                             110                                                                              30  5.0  0.20 8.00 × 10.sup.4                                                                 2.05 × 10.sup.6                                                               3.1 142.5                                                                             24.4                          16 rac-Me.sub.2 Si(Ind).sub.2 ZrMe.sub.2                                                    60 20  120  0.65 1.63 × 10.sup.4                                                                 2.34 × 10.sup.4                                                               3.59                                                                               145                                                                               --                            __________________________________________________________________________      .sup.a Carried out at 1 atm of ethylene and 50 mL of toluene on a high         vacuum line                                                                    .sup.b Reproducibility between runs = 10-15%                                   .sup.c GPC relative to polystyrene standards                                   .sup.d DSC from the second scan                                                .sup.e For propylene polymerization                                      

The table summarizes ethylene polymerization activities by various metallocene catalysts activated with Ph₃ C.sup.⊕ PBA.sup.⊖. Cp₂ ZrMe₂ exhibits virtually no activity for ethylene polymerization. This is presumably caused by the anion coordination through a Zr--F--Al bridge (FIG. 2a). However, as the ligand framework of the cation portion changes from Cp(C₅ H₅), to Cp"(1,2,-Me₂ C₅ H₃), to [1,3-(SiMe₃)₂ C₅ H₃ ], to Cp'(C₅ Me₅), the activity for ethylene polymerization increases dramatically (Examples 9-12) and reaches the highest level of 6.90×10⁶ g of PE/(mole of cat-atm-h) with the Cp'₂ ZrMe₂ catalyst (Example 12). The polyethylene produced is highly linear with a melting temperature T_(m) of 139.4° C. and crystalline with heat of fusion ΔHμ of 53.9 cal/g. As the bulkiness of cation portion increases, the degree of anion coordination drops significantly, clearly reflecting the relationship between the polymerization activity and the relative tightness of cation-anion pairing structure.

In the case of the Cp' ligand, the separation of cation and anion reaches an optimum condition for reactivity that results in the maximum polymerization activity and instability of the cationic complex derived therefrom as well. Such a dramatic influence of the ligand framework substituents on polymerization activity is unprecedented and suggests the special features of the subject anion. PBA.sup.⊖ is apparently such a large anion that separation of anion and cation can be easily and substantially tuned and optimized by selecting the appropriate bulky cation.

For the sterically more accessible CGC type of catalyst, PBA.sup.⊖ promotes no catalytic activity at room temperature, resulting from the strong anion coordination as reflected by the 66 ppm down-field shift of the Al--F F resonance as compared to PBA.sup.⊖ (FIG. 2c, Example 13). However, as the temperature of polymerization increases, the polymerization activity increases dramatically (Examples 13-15) presumably due to a higher degree of separation of cation-anion pairs at higher temperatures.

While the invention has been described with reference to a preferred embodiment, it will be understood by those skilled in the art that various changes may be made and equivalents may be substituted for elements thereof without departing from the scope of the invention. In addition, many modifications may be made to adapt a particular situation or material to the teachings of the invention without departing from the essential scope thereof. Therefore, it is intended that the invention not be limited to the particular embodiment disclosed as the best mode contemplated for carrying out this invention, but that the invention will include all embodiments and equivalents falling within the scope of the appended claims.

Various features of the invention are set forth in the following claims. 

What is claimed is:
 1. A method for polymerization of an alpha olefin which comprises polymerizing the alpha olefin in the presence of a catalystA)

    [CpCp'MR].sup.⊕ [ER'R"R'"F].sup.⊖

whereCp and Cp' is each a group containing a cyclopentadienyl ring; M is Ti, Zr, or Hf; R is CH₂ Ph, alkyl or aryl group (C≦20), or hydride; E is Al, Ga, or In; R', R", and R'" is each a fluorinated phenyl, fluorinated biphenyl or fluorinated polycyclic fused ring group; or B)

    [cp-A-Cp'Mr].sup.⊕ [ER'R"R'"F].sup.⊖

whereCp and Cp' is each a group containing a cyclopentadienyl ring; A is a bridging group M is Ti, Zr, or Hf; R is CH₂ Ph, alkyl or aryl group (C≦20), or hydride; E is Al, Ga, or In; and R', R", and R'" is each a fluorinated phenyl, fluorinated biphenyl or fluorinated polycyclic fused ring group; or C)

    [Me.sub.2 Si(C.sub.5 Me.sub.4)(.sup.t BuN)MR].sup.⊕ [ER'R"R'"F].sup.⊖

whereMe is methyl; N is nitrogen; M is Ti, Zr, or Hf; R is CH₂ Ph, alkyl or aryl group (C≦20), or hydride; E is Al, Ga, or In; and R', R", and R'" is each a fluorinated phenyl, fluorinated biphenyl or fluorinated polycyclic fused ring group.
 2. A method of claim 1 wherein E is aluminum.
 3. A method for polymerization of an alpha olefin of claim 1 which comprises polymerizing the alpha olefin in the presence of a catalyst of claim 1 of the formula

    [CpCp'MR].sup.⊕ [ER'R"R'"F].sup.⊖

whereCp and Cp' is each a group containing a cyclopentadienyl ring; M is Ti, Zr, or Hf; R is CH₂ Ph, alkyl or aryl group (C≦20), or hydride; E is Al, Ga, or In; R', R", and R'" is each a fluorinated phenyl, fluorinated biphenyl or fluorinated polycyclic fused ring group.
 4. A method of claim 3 wherein E is aluminum.
 5. A method of claim 4 wherein the catalyst is of the formula

    [(η.sup.5 -C.sub.5 H.sub.5).sub.2 Zr(CH.sub.2 Ph)].sup.⊕ [PBA].sup.⊖.


6. A method of claim 4 wherein the catalyst is of the formula

    [(η.sub.5 H.sub.3 Me.sub.2).sub.2 ZrMe)].sup.⊕ [PBA].sup.⊖.


7. A method of claim 4 wherein the catalyst is of the formula

    [{η.sup.5 -C.sub.5 H.sub.3 (SiMe.sub.3).sub.2 }.sub.2 Zr].sup.⊕ [PBA].sup.⊖.


8. A method of claim 4 wherein the catalyst is of the formula

    [(η.sup.5 -C.sub.5 Me.sub.5).sub.2 ZrMe].sup.⊕ [PBA].sup.⊖.


9. A method for polymerization of an alpha olefin of claim 1 which comprises polymerizing the alpha olefin in the presence of a catalyst of claim 4 of the formula

    [Cp-A-Cp'MR].sup.⊕ [ER'R"R'"F].sup.⊖

whereCp and Cp' is each a group containing a cyclopentadienyl ring; A is a bridging group which restricts the rotation of Cp and Cp' M is Ti, Zr, or Hf; R is CH₂ Ph, alkyl or aryl group (C≦20), or hydride; E is Al, Ga, or In; R', R", and R'" is each a fluorinated phenyl, fluorinated biphenyl or fluorinated polycyclic fused ring group.
 10. A method of claim 9 wherein E is aluminum.
 11. A method of claim 10 wherein the catalyst is of the formula

    [Me.sub.2 Si(Ind).sub.2 ZrMe].sup.⊕ [PBA].sup.⊖.


12. A method for polymerization of an alpha olefin of claim 1 which comprises polymerizing the alpha olefin in the presence of a catalyst of claim 1 of the formula

    [Me.sub.2 Si(η.sup.5 -C.sub.5 Me.sub.4)(.sup.t BuN)MR].sup.⊕ [ER'R"R'"F].sup.⊖

whereMe is methyl; N is nitrogen; M is Ti, Zr, or Hf; R is CH₂ Ph, alkyl or aryl group (C≦20), or hydride; E is Al, Ga, or In; and R', R", and R'" is each a fluorinated phenyl, fluorinated biphenyl or fluorinated polycyclic fused ring group.
 13. A method of claim 12 wherein E is aluminum.
 14. A catalytic complex selected from the group consisting of:A) a complex of the formula

    [CpCp'MR].sup.⊕ [ER'R"R'"F].sup.⊖

whereCp and Cp' is each a group containing a cyclopentadienyl ring; M is Ti, Zr, or Hf, R is CH₂ Ph, alkyl or aryl group (C≦20), or hydride; E is Al, Ga, or In; R', R", and R'" is each a fluorinated phenyl, fluorinated biphenyl or fluorinated polycyclic fused ring group; B) a complex of the formula

    [Cp-A-Cp'MR].sup.⊕ [ER'R"R'"F].sup.⊖

whereCp and Cp' is each a group containing a cyclopentadienyl ring; A is a bridging group M is Ti, Zr, or Hf, R is CH₂ Ph, alkyl or aryl group (C≦20), or hydride; E is Al, Ga, or In; R', R", and R'" is each a fluorinated phenyl, fluorinated biphenyl or fluorinated polycyclic fused ring group; and C) a complex of the formula

    [Me.sub.2 Si(η.sup.5 -C.sub.5 Me.sub.4)(.sup.t BuN)MR].sup.⊕ [ER'R"R'"F].sup.⊖

whereMe is methyl; N is nitrogen; M is Ti, Zr, or Hf; R is CH₂ Ph, alkyl or aryl group (C≦20), or hydride; E is Al, Ga, or In; and R', R", and R'" is each a fluorinated phenyl, fluorinated biphenyl or fluorinated polycyclic fused ring group.
 15. A complex of claim 14 wherein E is aluminum.
 16. A catalytic complex of claim 14 of the formula

    [CpCp'MR].sup.⊕ [ER'R"R'"F].sup.⊖

whereCp and Cp' is each a group containing a cyclopentadienyl ring; M is Ti, Zr, or Hf; R is CH₂ Ph, alkyl or aryl group (C≦20), or hydride; E is Al, Ga, or In; and R', R", and R'" is each a fluorinated phenyl, fluorinated biphenyl or fluorinated polycyclic fused ring group.
 17. A complex of claim 16 wherein E is aluminum.
 18. A complex of claim 17 wherein M is Zr.
 19. A complex of claim 18 of the formula

    [(η.sup.5 -C.sub.5 H.sub.5).sub.2 Zr((CH.sub.2 Ph)].sup.⊕ [PBA].sup.⊖.


20. 20. A complex of claim 18 of the formula

    [(η.sup.5 -C.sub.5 H.sub.3 Me.sub.2).sub.2 ZrMe)].sup.⊕ [PBA].sup.⊖.


21. A complex of claim 18 of the formula

    [{η.sup.5 -C.sub.5 H.sub.3 (SiMe.sub.3).sub.2 ZrMe].sup.⊕ [PBA].sup.⊖.


22. A complex of claim 18 of the formula

    [(η.sup.5 -C.sub.5 Me.sub.5).sub.2 ZrMe].sup.⊕ [PBA].sup.⊖.


23. A catalytic complex of claim 14 of the formula

    [Cp-A-Cp'MR].sup.⊕ [ER'R"R'"F].sup.⊖

whereCp and Cp' is each a group containing a cyclopentadienyl ring; A is a bridging group M is Ti, Zr, or Hf; R is CH₂ Ph, alkyl or aryl group (C≦20), or hydride; E is Al, Ga, or In; and R', R", and R'" is each a fluorinated phenyl, fluorinated biphenyl or fluorinated polycyclic fused ring group.
 24. A complex of claim 23 wherein E is aluminum.
 25. A complex of claim 24 wherein M is Zr.
 26. A complex of claim 25 of the formula

    [Me.sub.2 Si(Ind).sub.2 ZrMe].sup.⊕ [PBA].sup.⊖.


27. A catalytic complex of claim 14 of the formula

    [Me.sub.2 Si(η.sup.5 -C.sub.5 Me.sub.4)(.sup.t BuN)MR].sup.⊕ [Er'R"R'"F].sup.⊖

whereMe is methyl; N is nitrogen; M is Ti, Zr, or Hf; R is CH₂ Ph, alkyl or aryl group (C≦20), or hydride; E is Al, Ga, or In; and R', R", and R'" is each a fluorinated phenyl, fluorinated biphenyl or fluorinated polycyclic fused ring group.
 28. A complex of claim 27 wherein E is aluminum.
 29. A complex of claim 28 wherein M is Ti.
 30. A complex of claim 29 of the formula

    [Me.sub.2 Si(η.sup.5 -C.sub.5 Me.sub.4)(.sup.t BuN)TiMe].sup.⊕ [PBA].sup.⊖.


31. A complex of claim 28 wherein M is Zr.
 32. A complex of claim 31 of the formula

    [Me.sub.2 Si(η.sup.5 -C.sub.5 Me.sub.4)(.sup.t BuN)ZrMe].sup.⊕ [PBA].sup.⊖.


33. 33. A method of claim 2 wherein the catalyst is of the formula

    [Me.sub.2 Si(η.sub.5 -C.sub.5 Me.sub.4)(.sup.t BuN)TiMe].sup.⊕ [PBA].sup.⊖.


34. A method of claim 13 wherein the catalyst is of the formula

    [Me.sub.2 Si(η.sup.5 -C.sub.5 Me.sub.4)(.sup.t BuN)ZrMe].sup.⊕ [PBA].sup.⊖.


35. A method of any of claims 1-8 or 12, 13, 33, 34, wherein said alpha olefin is ethylene.
 36. A method of any of claims 7-11 wherein said alpha olefin is propylene.
 37. A method of any of claims 1-8 or 12-13 or 34 wherein said reaction is carried out at ambient conditions.
 38. A method of any of claims 9-13 or 33 wherein said reaction is initiated at temperatures from about 25° C. to about 110° C. 